HDPE: HCH 5110A 

product description

HCH 5110A has been manufactured using Basell Lupotech G licensed technology.

Recommended film thickness: 15 to 50µm. 

measurement

Film properties taken from 20µm blown film extruded at a melt temperature of 220˚C, long stalk process and a blow-up ration of 4:1.   

 

Resin Property
Value Units Test Method
Density
0.954
g/m3 ISO 1183
Melt Index (21.6) 23
g/10min
ISO 1133
Melt Index (5)
1.2 g/10min ISO 1133
FRR (21.6/5)
19


Molded Properties



Notched Impact @ 23°C 9 mJ/mm2
ISO 179/1 eA

Note: typical properties, not to be construed as specifications.


HDPE: HD-52518

 

product description

  • 52518 is a HDPE copolymer for injection molding for application requiring a good balance between easy of processability and flowability and mechanical properties. 

typical application

  • Housewares
  • High Fluidity

processing condition

Recommended barrel temperature range of 190°C to 280°C.

Storage and handling

  • Should not be stored in direct sunlight and/or heat.
  • Should be stored in a dry place, preferably under 50°C
  • It is recommended to process PE resin within 6 months after deliver. 
Resin Property
Value Units Test Method
Density
0.952
g/cc D 1505
Melt Index
18
g/10min
D 1238
Thermal Properties



Vicat Softening Point
122
°C D 1525
Molded Properties



Flexural Modulus
1350 MPa D 790
Notched Impact @ 23°C 25
J/m
D 256/A

Note: on compression molded according to ASTM D1928C.