LDPE Lupolen 2426 F

Product Description

  • Lupolen 2426 F is an additivated, low density Polyethylene and contains slip and anti-blocking agent.

 

Applications

  • Cast & Blown Film
  • Bags & Pouches
  • Film & Shrink Film
  • Food Packaging Film
  • Surface Protection Film

Processing method

  • Blown Film

Features

  • Unspecified Anti-blocking
  • Opticals
  • Good processability
  • Unspecified Slip
  • Low Friction

delivery

  • The product is delivered in pellet form. 

 

No.
Property
Value Units Test Method
1 Density 0.924 g/cm3 ISO 1183
2 Melt Flow Rate (MFR)(190°C/2.16Kg) 0.75 g/10 min
ISO 1133
3 Tensile Modulus
260 MPa ISO 527-1, -2
4 Tensile Stress at Yield
11 MPa ISO 527-1, -2
5 Tensile Strength MD/TD
26/20 MPa ISO 527-1, -3
6 Tensile Strain at Break MD/TD
300/600
% ISO 527-1, -3
7 Dart Drop Impact (50 blown film)
150 g ASTM D 1709
8 Vicat Softening temp (A50 (50°C/h 10N))
96 °C ISO 306
9 Haze (50)
<9.0 % ASTM D 1003
10 Glass (60°,50) >90 ASTM D 2457

Note: typical properties, not to be construed as specifications.


LDPE Lupolen 2420 D

Product description

  • Lupolen 2420 D is a non-additivated, low density Polyethylene. 

applications

  • Bags & Pouches
  • Bottles for Consumer Goods
  • Shrink Film
  • Blown Film
  • Film

processing method

  • Blown Film
  • Injection Moulding
  • Extrusion Blow Moulding

Features

  • Good Processability
  • Good Tear Strength 
  • Good Toughness

Delivery

  • The product is delivered in pellet form. 

 

No.
Property
Value Units Test Method
1 Density 0.923 g/cm3 ISO 1183
2 Melt Flow Rate (MFR)(190°C/2.16Kg) 0.25 g/10 min
ISO 1133
3 Tensile Modulus
240 MPa ISO 527-1, -2
4 Tensile Stress at Yield
10 MPa ISO 527-1, -2
5 Tensile Strength MD/TD
27/20 MPa ISO 527-1, -3
6 Tensile Strain at Break MD/TD
200/500
% ISO 527-1, -3
7 Dart Drop Impact (50 blown film)
250 g ASTM D 1709
8 Vicat Softening temp (A50 (50°C/h 10N))
94 °C ISO 306
9 Haze (50)
<14 % ASTM D 1003
10 Glass (60°,50) >50 ASTM D 2457

Note: typical properties, not to be construed as specifications.