LFI2130

Product Description

  • LFI2130 is a high molecular weight low density polyethylene film grade, combining good flexible extrusion behavior and superior mechanical properties.

 

Applications

  • LFI2130 is suitable for general packaging applications, particularly those requiring a measure of shrink.

 

Processing

  • LFI2130 ia  grade with excellent toughness and outstanding biaxial shrink properties. The material contains only antioxidant, has very low energy consumption during processing and has excellent de\raw down ability. 

 

 

For more information please contact us: info@commgate.co.uk

Property
Value Units Test Method
Density
921
Kg/m3 ISO 1183(A)
Melt Index (190°C/2.16Kg) 0.3 g/10min
ISO 1133
Impact Strength
31
KJ/m
ASTM D4272
Tear Strength (TD/MD)
45/20
kN/m
ISO 6383
Yield Stress TD/MD
10/11 MPa
ISO 527
Strain at Break (TD/MD)
>500/>350
%
ISO 527
Modulus of Elasticity (TD/MD)
150/140 MPa ISO 527
Coefficient of Friction
0.7 - ASTM D1894
Blocking
<5 g Sabtec
Re-blocking 20 g Sabtec
Haze 12 % ASTM D1003A
Gloss 55 % ASTM D2457
Clarity 50 mV Sabtec

Note: typical properties, not to be construed as specifications.


LDPE 2420 D

Product description

  • 2420 D is a non-additivated, low density Polyethylene. 

applications

  • Bags & Pouches
  • Bottles for Consumer Goods
  • Shrink Film
  • Blown Film
  • Film

processing method

  • Blown Film
  • Injection Moulding
  • Extrusion Blow Moulding

Features

  • Good Processability
  • Good Tear Strength 
  • Good Toughness

Delivery

  • The product is delivered in pellet form. 

 

 

No.
Property
Value Units Test Method
1 Density 0.923 g/cm3 ISO 1183
2 Melt Flow Rate (MFR)(190°C/2.16Kg) 0.25 g/10 min
ISO 1133
3 Tensile Modulus
240 MPa ISO 527-1, -2
4 Tensile Stress at Yield
10 MPa ISO 527-1, -2
5 Tensile Strength MD/TD
27/20 MPa ISO 527-1, -3
6 Tensile Strain at Break MD/TD
200/500
% ISO 527-1, -3
7 Dart Drop Impact (50 blown film)
250 g ASTM D 1709
8 Vicat Softening temp (A50 (50°C/h 10N))
94 °C ISO 306
9 Haze (50)
<14 % ASTM D 1003
10 Glass (60°,50) >50 ASTM D 2457

Note: typical properties, not to be construed as specifications.


LTM 2125/37

Property
Value Units Test Method
Density
921
Kg/m3 ISO 1183(A)
Melt Index (190°C/2.16Kg) 2.5
g/10min
ISO 1133
Impact Strength
23
KJ/m
ASTM D4272
Tear Strength (TD/MD)
25/70
kN/m
ISO 6383
Yield Stress TD/MD
11/13
MPa
ISO 527
Tensile Stress at Break (MD/TD)
19/30 MPa ISO 527
Strain at Break (TD/MD)
>500/>100
%
ISO 527
Modulus of Elasticity (TD/MD)
180/190 MPa ISO 527
Coefficient of Friction
0.2 - ASTM D1894
Blocking
<5 g Sabtec
Re-blocking 0
g Sabtec
Haze 9
% ASTM D1003A
Gloss 60
% ASTM D2457
Clarity 30
mV Sabtec

Description

LTM 2125/37 has been manufactured using SABTEC licensed technology.

Application

LTM 2125/37 is suitable for packaging films and is especially suitable when ultimate down gauging is required.

Measurement

Film properties have been measured at 25µm with a BUR of 3.

 

 

Note: typical properties, not to be construed as specifications.


LTM 2185/47

Property
Value Units Test Method
Density
921
Kg/m3 ISO 1183(A)
Melt Index (190°C/2.16Kg) 0.85
g/10min
ISO 1133
Impact Strength
30
KJ/m
ASTM D4272
Tear Strength (TD/MD)
30/40
kN/m
ISO 6383
Yield Stress TD/MD
11/12
MPa
ISO 527
Tensile Stress at Break (MD/TD)
21/24 MPa ISO 527
Strain at Break (TD/MD)
>500/>200
%
ISO 527
Modulus of Elasticity (TD/MD)
170/160 MPa ISO 527
Coefficient of Friction
0.1 - ASTM D1894
Blocking
10
g Sabtec
Re-blocking 30
g Sabtec
Haze 11
% ASTM D1003A
Gloss 55
% ASTM D2457
Clarity 37
mV Sabtec

description

LTM 2185/47 has been manufactured using SABTEC licensed technology.

Application

LTM 2185/47 can be used for shrink packaging applications.

measurements

Film properties have been measured at 25µm with a BUR of 3.

 

 


LTM2119X

description

Property
Value Units Test Method
Density
921
Kg/m3 ISO 1183(A)
Melt Index (190°C/2.16Kg) 0.85
g/10min
ISO 1133
Impact Strength
30
KJ/m
ASTM D4272
Tear Strength (TD/MD)
30/40
kN/m
ISO 6383
Yield Stress TD/MD
11/12
MPa
ISO 527
Tensile Stress at Break (MD/TD)
21/24 MPa ISO 527
Strain at Break (TD/MD)
>500/>200
%
ISO 527
Modulus of Elasticity (TD/MD)
170/160 MPa ISO 527
Coefficient of Friction
0.1 - ASTM D1894
Blocking
10
g Sabtec
Re-blocking 30
g Sabtec
Haze 11
% ASTM D1003A
Gloss 55
% ASTM D2457
Clarity 37
mV Sabtec

LTM 2119X has been manufactured using SABTEC licensed technology.

Application

LTM 2119X is suitable for general purpose film and for lamination.

measurements

Film properties have been measured at 25µm with a BUR of 3.