LLDPE: LL0209AA

product description

  •  “LL 0209AA” is a LLDPE copolymer with butene as comonomer which contains antioxidant.
  • Recommended for general purpose applications.
  • Suitable for blending with conventional LDPE.

Film made from pure LL 02090 AA has the following advantages over conventional LDPE:

  • Better sealing,higher puncture resistance.
  • Greater drawdown capability.
  • Higher tensile strength.

Neutralizer: Calcium Stearate
Antioxidant: Irganox1010, Irganox168

applications

  • Food Grade
  • Heavy Duty Sacks
  •  Agricultural Films
  • Liners
  • Produce Bags
  • Stretch Films
Property
Value Units Test Method
Density
920
Kg/m3 ISO 1181
Melt Index (190°C/2.16Kg) 0.9 g/10min
ISO 1133
Tensile Strength at Yield MD/TD
10/11 MPa ISO 527
Tensile Strength at Break MD/TD
620/840
% ISO 527
Tear Strength MD/TD
145/370 g/25µ ASTM D 1922
Dart Drop Impact
130 g ASTM D1709

Note: typical properties, not to be construed as specifications.

For more information please contact us: info@commgate.co.uk


LLDPE: 22501AA/22501KJ

PRODUCT DESCRIPTION

  • 22501 is a LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications. 

Features

  • High Stiffness
  • Good Optical Properties
  • Low Extrusion Temperature 
  • Ease of Processing
  • Low Gels 
  • Suited for Blending with LDPE
  • General Purpose Applications

applications

  • Blown Film Grade

additives

  • 22501AA: Thermal Antioxidant
  • 22501KJ: Thermal Antioxidant, Antiblocking Agent, Slip Agent 

recommended processing conditions

  • Melt Temperature (°C): 190-230
  • low up Ration: 2.0-3.0
  • Die Gap (mm): 2.0-2.5
  • Thickness (micron): 15-150

 

Resin Property
Value Units Test Method
Density 0.9220 g/cm3 D 1505
Melt Index
0.95 g/10 min
D 1238
Film Properties



Dart Impact
80 g D 1709
Elmendorf Tear MD/TD
105/460 g D 1922
Tensile Strength at Break MD/TD
45/30
MPa D 882
Tensile Strength at Yield MD/TD
13/12.5 MPa
D 882
Ultimate Elongation MD/TD
680/780 % D 882
2% Secant Modulus MD/TD
200/240 MPa
D 882
Haze
21 % D 1003
Gloss (45°) 38 D 2457
@ 25 micron film obained on collin 25, B.u.R. 2.5: l, Temp. profile 155 -> 190°C

Note: typical properties, not to be construed as specifications.